Probing the effects of thermal treatment on the electronic structure and mechanical properties of Ti-doped ITO thin films
Journal article   Open access   Peer reviewed

Probing the effects of thermal treatment on the electronic structure and mechanical properties of Ti-doped ITO thin films

H. Taha, D.J. Henry, C-Y Yin, A. Amri, X. Zhao, S. Bahri, C. Le Minh, N.N. Ha, M.M. Rahman and Z-T Jiang
Journal of Alloys and Compounds, Vol.721, pp.333-346
2017
DOI: https://doi.org/10.1016/j.jallcom.2017.06.007
pdf
probing-the-effects-of-thermal-treatment.pdfDownloadView
Author’s VersionCC BY-NC-ND V4.0,  Open Access
url
Link to Published Version *Subscription may be requiredView

Abstract

Titanium-doped indium tin oxide thin films were synthesized via a sol-gel spin coating process. Surface chemical bonding states and mechanical properties have been investigated as a function of titanium content (2 and 4 at%) and annealing temperature ranging from 400 to 600 °C with increments of 100 °C. Raman analysis was performed to study the phonon vibrations for the prepared samples and the results revealed the existence of ITO vibrational modes. The elemental compositions, bonding states and binding energies of the film materials were investigated using X-ray photoelectron spectroscopy (XPS) technique. The XPS results indicated that the ratio of the metallic elements (In, Sn, Ti) to the oxygen on the surface of the thin film coatings decreased due to the increase of the oxide layer on the surface of the thin films. Also, by increasing the annealing temperature up to 600 °C, the Ti 2p and Cl 2p signals were no longer detected for both 2 and 4 at% Ti contents, respectively, due to the thicker surface oxidation layer. Mechanical properties of the synthesized films were also evaluated using a nanoindentation process. Variations in the hardness (H) and the elastic modulus (E) were observed with different Ti at% and annealing temperatures. The hardness is within the range of 6.3–6.6 GPa and 6.7–6.8 GPa for 2 and 4 at% Ti content samples, respectively, while the elastic modulus is within the ranges of 137–143 and 139–143 GPa for 2 at% and 4 at% Ti contents samples, respectively. A combination of the highest H and E were achieved in the sample of 4% Ti content annealed at 600 °C. Furthermore, the H/E ratio ranges from 4.5 × 10−2 to 5.0 × 10−2 which reflects a reasonable level of wear resistance.

Details

Metrics

108 File views/ downloads
45 Record Views
18 Times Cited - Web of Science

InCites Highlights

These are selected metrics from InCites Benchmarking & Analytics tool, related to this output

Collaboration types
Domestic collaboration
International collaboration
Citation topics
2 Chemistry
2.74 Photocatalysts
2.74.16 ZnO Nanostructures
Web Of Science research areas
Chemistry, Physical
Materials Science, Multidisciplinary
Metallurgy & Metallurgical Engineering
ESI research areas
Materials Science
Logo image